Semiconductor device and manufacturing method thereof

ABSTRACT

A method for producing a thin-film transistor by using a crystalline silicon film that has been formed by using nickel as a metal element for accelerating crystallization of silicon. In forming source and drain regions, phosphorus as an element for gettering nickel is introduced therein by ion implantation. Nickel gettering is effected by annealing. For example, in the case of producing a P-channel thin-film transistor, both phosphorus and boron are used. Boron determines a conductivity type, and phosphorus is used as a gettering material.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a doping technique in a manufacturing process of an insulated-gate semiconductor device, such as a thin-film transistor (TFT), having a non-single-crystal crystalline silicon film and other semiconductor devices which doping technique minimizes adverse effects on such a device of an impurity (e.g., Ni) contained in the crystalline silicon film. The invention is particularly advantageous when the crystalline silicon film is one that has been formed with the aid of a crystallizing catalyst element (e.g., Ni).

[0003] 2. Description of the Related Art

[0004] In recent years, various studies have been made of insulated-gate semiconductor devices having a thin-film active layer (active region) on an insulative substrate. In particular, a thin-film, insulated-gate transistor, i.e., what is called a thin-film transistor (TFT) has been studied enthusiastically. Thin-film transistors are classified into an amorphous silicon TFT, a crystalline silicon TFT, etc. depending on the material and the crystal state of a semiconductor used. Since “crystalline silicon” mentioned above is non-single-crystal silicon, the above TFTs are generically called non-single-crystal TFTs.

[0005] In general, amorphous semiconductors have small electric field mobilities, and therefore cannot be used for a TFT that is required to operate at high speed. Further, P-type amorphous silicon has a very small electric field mobility, which means that amorphous silicon cannot provide a P-channel TFT (PMOS TFT). Therefore, amorphous silicon does not allow formation of a complementary MOS (CMOS) circuit by combining P-channel TFTs and N-channel TFTs (NMOS TFTs).

[0006] On the other hand, crystalline semiconductors have larger electric field mobilities than amorphous semiconductors, and hence enable high-speed operation. Since crystalline silicon can provide a PMOS TFT as well as an NMOS TFT, it allows formation of a CMOS circuit.

[0007] A non-single-crystal crystalline silicon film can be obtained by thermally annealing, for a long time at a proper temperature (usually more than 600° C.), an amorphous silicon film that has been produced by vapor-phase growth, or by application of strong light such as laser light (optical annealing).

[0008] In the thermal annealing method, as described in Japanese Unexamined Patent Publication No. Hei. 6-244104, a crystalline silicon film can be obtained by a thermal annealing process that is shorter and lower in temperature than usual cases by using an effect that an element such as nickel, iron, cobalt, platinum, palladium, or the like (hereinafter called a crystallizing catalyst element or simply a catalyst element) accelerates crystallization of amorphous silicon.

[0009] Similar techniques are disclosed in Japanese Unexamined Patent Publication Nos. Hei. 6-318701, 6-333951, etc. It has also been revealed that in a silicon film having such a crystallizing catalyst element, thermal annealing that is lower in temperature than conventional cases enables activation of an impurity element which is performed after impurity regions such as a source and a drain are formed by implanting N-type or P-type impurity ions by ion doping or the like. (Japanese Unexamined Patent Publication Nos. Hei. 6-267980 and Hei. 6-267989)

[0010] For the above purpose, it is desired that the concentration of a crystallizing catalyst element be 1×10¹⁵ to 1×10¹⁹ atoms/cm³. Crystallization is not accelerated if the concentration is lower than this range, while the characteristics of a silicon semiconductor are impaired if the concentration is higher than this range. It is noted that the concentration of a catalyst element is defined as a maximum of values obtained by an analysis according to the secondary ion mass spectrometry (SIMS). In many cases, a catalyst element is distributed in a film.

[0011] Although semiconductor devices produced by using a crystalline silicon film containing a catalyst element for accelerating crystallization have a large electric field mobility, many of those exhibit a large off-current. In particular, where a large number of semiconductor devices are formed on the same substrate, large off-currents, which in itself are undesirable, have a large variation among the semiconductor devices.

[0012] Large off-currents and their large variation are believed due to the existence of the catalyst element for accelerating crystallization; that is, mainly due to the fact that the catalyst element exists in junctions.

[0013] In particular, the above undesired characteristics are fatal to TFTs that constitute a pixel section of a liquid crystal display.

SUMMARY OF THE INVENTION

[0014] Among semiconductor devices produced by using a crystalline silicon film into which nickel was introduced as a catalyst element for accelerating crystallization, those whose impurity regions (sources and drains, etc.) were formed by implanting phosphorus showed relatively low off-currents (about 10 pA or less) with almost no variation. Based on this fact, the inventors have studied properties of phosphorus in detail, and have found a report stating that phosphorus has a feature of gettering impurities.

[0015] According to this report, phosphorus shows a particularly high degree of gettering function with respect to nickel. Further, elements, such as copper and iron, which are considered to adversely affect semiconductor devices, can be gettered by phosphorus. This lead to an assumption that in the above semiconductor devices, phosphorus neutralizes the properties of nickel in a certain manner, to thereby suppress the adverse effects of nickel on the off-current characteristic.

[0016] The invention utilizes the gettering function of phosphorus with respect to nickel. “The gettering function” is defined as operation that phosphorus captures nickel, thereby reducing the effects of nickel.

[0017] For example, process for manufacturing a n-channel type thin film transistor using the nickel function will be explained as follows.

[0018] First, source and drain regions are formed by doping phosphorus ions using a gate electrode as a mask.

[0019] A channel region and n-type source and drain regions are formed in an active region of the thin film transistor by the phosphorus ion doping

[0020] After that, thermal annealing or laser annealing is performed. In this process, nickel elements are removed from the channel region that no phosphorus is doped by the function of phosphorus doped in the source and drain regions.

[0021] That is, the nickel elements are captured by phosphorus and thereby the nickel elements are transferred from the channel region into the source and drain regions.

[0022] In the result of the thermal annealing or laser annealing process described above, the nickel elements gather into the source and drain regions. On the other hand, nickel elements are reduced in the region that no phosphorus is doped. The nickel elements doped highly in the channel region affects operation of the thin film transistor adversely.

[0023] In operation of the thin film transistor, it is required that resistance of the channel region is slightly changed by a voltage applied for the gate electrode. That is, slight change of electric property is needed for the channel region. However, the nickel disturbs the slight change.

[0024] Consequently, the Off-current is increased and the characteristics of the thin film transistor fluctuates.

[0025] On the other hand, even if nickel is highly doped in the source and drain regions, the off-current is not almost increased and the characteristic does not almost affect.

[0026] Accordingly, it is excessively effective for enhancing the characteristic of the thin film transistor to change distribution of nickel in the active region, that is, to increase concentration of nickel in source and drain regions and reduce concentration thereof in the channel region, relatively.

[0027] Where a p-channel type thin film transistor is manufactured, phosphorus ions are doped into the source and drain regions and p-type impurities are doped therein to invert the conductivity type. Thereby, the nickel is transferred into the source and drain regions.

[0028] In the invention described above, the catalyst element for accelerating crystallization may be a metal element such as nickel, platinum, cobalt, iron, palladium, or the like. Among those elements, nickel is particularly superior in the effect of accelerating crystallization of silicon.

[0029] It is preferred that the concentration of the catalyst element be set in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³. If the concentration is lower than 1×10¹⁵ atoms/cm³, the effect of accelerating crystallization is not attained. On the other hand, if the concentration is higher than 1×10¹⁹ atoms/cm³, silicon partly assumes metallic properties to lose its semiconductor characteristics. It is noted that in this specification the concentration of a catalyst element in a silicon film is defined as a maximum of values obtained by an analysis and a measurement according to the secondary ion mass spectrometry (SIMS).

BRIEF DESCRIPTION OF THE DRAWINGS

[0030]FIGS. 1A to 1F show a manufacturing process of a thin-film transistor according to first and second embodiments of the present invention;

[0031]FIGS. 2A to 2F show a manufacturing process of a thin-film transistor according to a third embodiment of the invention;

[0032]FIG. 3 shows a thin-film transistor according to a fourth embodiment of the invention; and

[0033]FIGS. 4A to 4H show a manufacturing process of a thin-film transistor according to a seventh embodiment of the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0034] Embodiment 1

[0035] This embodiment is directed to a method of producing an N-type semiconductor device having superior characteristics by forming an uncompleted transistor on a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization has been introduced, then implanting ions including phosphorus ions into its source and drain regions by known ion doping (also called plasma doping) or ion implantation, and finally improving the crystallinity of the silicon film and activating impurities by thermal annealing or optical annealing (or both). In the following, “semiconductor devices having superior characteristics” means semiconductor devices in which off-currents are about 10 pA or less and variations of characteristics among devices are small. FIGS. 1A to 1F show a manufacturing process of this embodiment.

[0036] First, a 2,000-Å-thick undercoat silicon oxide film 102 and a 500-Å-thick amorphous silicon film 103 are sequentially formed on a glass substrate (Corning 7059 in this embodiment) 101 by plasma CVD. A nickel acetate layer (not shown) is formed on the above structure by applying a nickel acetate aqueous solution of 10 ppm and performing spin coating. It is preferred that a surface active agent be added to the nickel acetate aqueous solution. (FIG. 1A)

[0037] Thereafter, thermal annealing is performed at 550° C. for 4 hours to crystallize the amorphous silicon film 103, i.e., obtain a crystalline silicon film 104. In this process, nickel serves as crystal nuclei, thereby accelerating crystallization of the amorphous silicon film 103.

[0038] It is due to this action of nickel that the above thermal annealing can be performed under the low-temperature (lower than the strain temperature of Corning 7059), short-time conditions of 550° C. and 4 hours. Details of the above steps are described in Japanese Unexamined Patent Publication No. Hei. 6-244104.

[0039] It is preferred that the concentration of the catalyst element be set in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³. In this embodiment, the concentration of the catalyst element in the silicon film is 1×10¹⁷ to 5×10¹⁸ atoms/cm³ in terms of a minimum value in the film, which concentration is defined as a maximum of values obtained by an analysis and a measurement according to the secondary ion mass spectrometry (SIMS).

[0040] To improve the crystallinity of the above-obtained crystalline silicon film 104, it is illuminated with light emitted from an excimer laser that is a high-power pulsed laser. In this embodiment, a KrF excimer laser (wavelength: 248 nm; pulse width: 30 nsec) is used. The energy density of laser light is selected from a range of 100 to 500 mJ/cm² so as to provide the crystalline silicon film 104 with best crystallinity. In this embodiment, the laser light energy density is set at 370 mJ/cm². Where the area of an illumination object is larger than the beam size of the excimer laser light, the illumination is performed while the laser beam is moved relative to the illumination object. The illumination is so performed that each point on the illumination object receives 2 to 20 shots of laser light. The substrate temperature is kept at 200° C. during the laser light illumination. (FIG. 1B)

[0041] Then, the crystalline silicon film 104 is etched into an island-like silicon region 105. A 1,200-Å-thick silicon oxide film 106 as a gate insulating film is deposited thereon by plasma CVD using TEOS as a material gas, with the substrate temperature kept at 250 to 380° C., for instance, 300° C. (FIG. 1C)

[0042] Subsequently, an aluminum film (containing silicon at 0.1 to 2%) is deposited by sputtering at a thickness of 3,000 to 8,000 Å, for instance, 6,000 Å, and then etched to form a gate electrode 107. (FIG. 1C)

[0043] Thereafter, phosphorus ions are implanted into the island-like silicon region 105 with the gate electrode 107 used as a mask. Phosphine (PH₃) that is diluted with hydrogen to 1 to 10% is used as a doping gas. The acceleration voltage is set at 60 to 90 kV, for instance, 80 kV, and the dose is set at 1×10¹³ to 8×10¹⁵ atoms/cm³, for instance, 2×10¹⁴ atoms/cm³. Under these conditions, phosphorus ions are introduced into the island-like region 105 at a concentration of 3×10¹⁹ atoms/cm³. Thus, N-type impurity regions 108 (source) and 109 (drain)and a channel region 100 are formed. (FIG. 1D)

[0044] According to the experiences of the inventors, the preferable range of concentration of an impurity for imparting N-type or P-type conductivity in a silicon region is 3×10¹⁹ to 1×10²¹ atoms/cm³. The substrate is kept at the room temperature during the ion doping.

[0045] Then, to activate phosphorus (dopant) and to cause phosphorus to getter nickel, optical annealing is performed by using a KrF excimer laser. The energy density of laser light is set at 100 to 350 mJ/cm², for instance, 250 mJ/cm². Where the area of an illumination object is larger than the beam size of excimer laser light, the illumination is performed while the laser beam is moved relative to the illumination object. The illumination is so performed that each point on the illumination object receives 2 to 20 shots of laser light. The substrate temperature is kept at 200° C. during the laser light illumination. Then, thermal annealing is performed at 350° C. for 2 hours in a nitrogen atmosphere. Although both optical annealing and thermal annealing are performed in this embodiment, only one of those may be performed.

[0046] In the annealing process, nickel in the channel region 100 is transferred into the source region 108 and drain region 109. Thereby, concentration of nickel in the channel region 100 can be reduced. (FIG. 1E)

[0047] Subsequently, a 6,000-Å-thick silicon oxide film 110 as an interlayer insulating film is deposited by plasma CVD, and contact holes are formed therein. After a metal material, for instance, a multi-layer film of titanium and aluminum films is deposited and patterned to form electrode/wiring lines 111 and 112 of the source and drain of a TFT. Finally, thermal annealing is performed at 200 to 350° C. in a hydrogen atmosphere of 1 atm. (FIG. 1F)

[0048] Embodiment 2

[0049] This embodiment is directed to a method of producing a P-type semiconductor device having superior characteristics in a process of manufacturing a transistor by using a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization has been introduced. More specifically, ions including phosphorus ions are implanted into source and drain regions of the crystalline silicon film by known ion doping (also called plasma doping), then a P-type impurity ions (in this embodiment, ions including boron ions) are further implanted into the silicon film, and finally thermal annealing or optical annealing (or both) is performed to improve the crystallinity of the silicon film and activate impurities.

[0050] This embodiment may be implemented by adding a step of implanting P-type impurity ions (in this embodiment, ions including boron ions) into the source and drain regions. This step may be performed before or after the phosphorus ion doping shown in FIG. 1D. Only the additional step of doping with P-type impurity ions will be described below.

[0051] In this embodiment, boron ions as P-type impurity ions are implanted into the silicon region 105 with the gate electrode 107 used as a mask. Diborane (B₂H₆) that has been diluted with hydrogen to 5% is used as a doping gas. The acceleration voltage is set at 60 to 90 kV, for instance, 80 kV, and the dose is set at 1×10¹³ to 8×10¹⁵ atoms/cm³, for instance, 4×10¹⁴ atoms/cm³.

[0052] In this step, the dose is so adjusted that the maximum concentration value of boron in the source and drain regions minus that of phosphorus in the same regions becomes 3×10¹⁹ to 1×10²¹ atoms/cm³. The substrate is kept at the room temperature during the ion doping. Thus, P-type impurity regions 108 (source) and 109 (drain) and channel region 100 are formed.

[0053] In this embodiment, in forming the P-type TFT, not only the impurity for imparting P-type conductivity such as boron but also nickel and phosphorus are added to the active layer made of a crystalline silicon film. Therefore, a silicon film having good crystallinity can be obtained at a low temperature in a short time due to the catalyst effect of nickel, and nickel that has become unnecessary can be gettered by phosphorus. As a result, this embodiment can produce TFTs having superior electrical characteristics whose variations among devices are small.

[0054] That is, concentration of nickel in the channel region 100 can be reduced. Thereby, the thin film transistor having high characteristics and low fluctuation thereof can be obtained.

[0055] Embodiment 3

[0056] This embodiment is directed to a method of separately producing N-type and P-type semiconductor devices having superior characteristics on the same substrate by forming a plurality of uncompleted transistors on a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization, then implanting ions including phosphorus ions into their source and drain regions by known ion doping (also called plasma doping), and finally selectively implanting P-type impurity ions (in this embodiment, ions including boron ions).

[0057]FIGS. 2A to 2F shows a manufacturing process of CMOS TFTs according to this embodiment. First, as shown in FIG. 2A, an undercoat silicon oxide film 202 is deposited on a glass substrate (Corning 1737) 201 at a thickness of 1,000 to 5,000 Å, for instance, 2,000 Å, by plasma CVD using monosilane and nitrogen monoxide as materials. A 1,000-Å-thick amorphous silicon film 203 is deposited thereon by plasma CVD using monosilane as a material.

[0058] Thereafter, a very thin silicon oxide film (not shown) is formed on the surface of the amorphous silicon film 203 by using an aqueous solution of hydrogen peroxide. An acetate salt solution containing nickel at 1 to 30 ppm, for instance, 10 ppm, is applied by spin coating and then dried to form a catalyst layer 204 containing nickel. (FIG. 2A)

[0059] Subsequently, thermal annealing is performed at 550° C. for 4 hours in a nitrogen atmosphere to crystallize the amorphous silicon film 203. In this process, nickel moves from the amorphous silicon film 203 to the undercoat silicon oxide film 203, and crystallization proceeds downward.

[0060] After the crystallization step by thermal annealing, XeCl laser light (wavelength: 308 nm) is applied to the crystallized silicon film to enhance its crystallinity.

[0061] Then, as shown in FIG. 2B, the crystallized silicon film is etched into island-like silicon regions 205 and 206. A 1,000-Å-thick silicon oxide film 207 as a gate insulating film is deposited thereon by plasma CVD using monosilane and nitrogen monoxide as materials.

[0062] Subsequently, an aluminum film (containing scandium at 0.1 to 2%) is deposited by sputtering at a thickness of 3,000 to 8,000 Å, for instance, 4,000 Å, and then etched to form gate electrodes 208 and 209.

[0063] Then, as shown in FIG. 2C, the island-like silicon regions 205 and 206 are doped with phosphorus ions by ion doping in a self-aligned manner with the gate electrodes 208 and 209 used as a mask. Phosphine (PH₃) that is diluted with hydrogen to 1 to 10% is used as a doping gas. The acceleration voltage may be set at 60 to 90 kV, and the dose may be set at 1×10¹³ to 8×10¹⁵ atoms/cm³. In this embodiment, the acceleration voltage is set at 80 kV, and the dose is set at 2×10¹⁴ atoms/cm³. Under these conditions, phosphorus ions are introduced into the island-like silicon regions 205 and 206 at a concentration of 3×10¹⁹ atoms/cm³, so that N-type impurity regions 210 to 213 are formed.

[0064] Thereafter, as shown in FIG. 2D, a region to become an N-type TFT is covered with a resist mask 214 by a known photoresist method. In this state, P-type impurity ions (in this embodiment, boron ions) are introduced into the island-like silicon region 206 by ion doping with the gate electrode 209 used as a mask. Diborane (B₂H₆) that is diluted with hydrogen to 5% is used as a doping gas. The acceleration voltage may be set at 60 to 90 kV, and the dose may be set at 1×10¹³ to 8×10¹⁵ atoms/cm³. In this embodiment, the acceleration voltage is set at 80 kV and the dose is set at 4×10¹⁴ atoms/cm³. As a result, the conductivity type of the N-type impurity regions 212 and 213 of the island-like silicon region 206 is inverted to form P-type impurity regions 215 (source) and 216 (drain). On the other hand, the N-type conductivity of the impurity regions 210 and 211 that are covered with the resist mask 214 is maintained.

[0065] In the above step, the dose is so adjusted that the maximum concentration of boron in the source and drain regions 215 and 216 minus that of phosphorus in those regions becomes 3×10¹⁹ to 1×10²¹ atoms/cm³. The substrate is kept at the room temperature during the ion doping.

[0066] Although in this embodiment boron ions are introduced after the phosphorus ion implantation, they may be introduced before the phosphorus ion implantation. In the latter case, as shown in FIG. 2D, boron ions are introduced in a state that the N-type TFT region is covered with a mask 214. Phosphorus ions may be introduced after the resist mask 214 is removed.

[0067] Then, after the resist mask 214 is removed, laser annealing is performed as shown in FIG. 2E to activate the added impurities and to restore the crystallinity of the island-like silicon regions 205 and 206 that have been damaged in the doping step. In this embodiment, since phosphorus is added to the N-type impurity regions 210 and 211 and the P-type impurity regions 215 and 216 at a concentration of 3×10¹⁹ atoms/cm³, nickel is gettered by phosphorus upon laser light illumination. KrF excimer laser light (wavelength: 248 nm) is used. To getter nickel effectively, it is preferred that the laser light illumination conditions be such that the energy density is 200 to 400 mJ/cm², for instance, 250 mJ/cm², each point receives 2 to 20 shots of laser light, and the substrate temperature during the laser light illumination is set at 200° C.

[0068] In this process, nickel in the channel regions 21 and 22 is transferred into the source and drain regions 210,211,212 and 213 that phosphorus is doped. Thereby, concentration of nickel in the channel region 21 and 22 can be reduced.

[0069] After the laser annealing, thermal annealing is performed at 350° C. for 2 hours in a nitrogen atmosphere. Although both laser annealing and thermal annealing are performed in this embodiment, only one of those may be performed.

[0070] Subsequently, as shown in FIG. 2F, a 6,000-Å-thick silicon oxide film 216 as an interlayer insulating film is formed by plasma CVD. After contact holes are formed in the interlayer insulating film 217, electrodes/wiring lines 218 to 220 of the N-type and P-type TFTs are formed by using a metal material, for instance, a multi-layer film of titanium film and an aluminum film. Finally, a thermal treatment is performed at 350° C. for 2 hours in a hydrogen atmosphere. (FIG. 2F)

[0071] With the above steps, CMOS TFTs are completed in which the N-type TFT and the P-type TFT are combined complementarily.

[0072] Embodiment 4

[0073] This embodiment is directed to a method of producing an N-type semiconductor device having superior characteristics in manufacturing a thin-film transistor having a LDD structure by using a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization has been introduced. More specifically, ions including phosphorus ions are implanted into source and drain regions and LDD regions by known ion doping (also called plasma doping), and then thermal annealing or optical annealing (or both) is performed to improve the crystallinity of the silicon film and activate impurities.

[0074] The same steps as in the first embodiment are employed until formation of a crystalline silicon film. Thereafter, a thin-film transistor having a known LDD structure is formed by a known method. The source and drain regions and the LDD regions are activated in the same manner as in the first embodiment. FIG. 3 shows a TFT of a LDD structure having side walls.

[0075] As shown in FIG. 3, lightly doped impurity regions 302 having a lower impurity concentration than source and drain regions 301 are formed between the source and drain regions 301 and the channel region. One of the lightly doped impurity regions 302 which is located on the drain side is particularly called a LDD region.

[0076] In this embodiment, phosphorus is implanted in the source and drain regions 301 at 1×10²⁰ to 1×10²¹ atoms/cm², and it is implanted in the lightly doped impurity regions 302 at 4×10¹⁶ to 7×10¹⁷ atoms/cm³. With the doping of such concentrations, phosphorus can effectively getter nickel that has become unnecessary. Therefore, TFTs can be obtained in which the characteristics have only small variations among devices and off-currents are small.

[0077] Embodiment 5

[0078] This embodiment is directed to a method of producing a P-type semiconductor device having superior characteristics in manufacturing a thin-film transistor having a LDD structure by using a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization has been introduced. More specifically, ions including phosphorus ions are implanted into LDD regions by known ion doping (also called plasma doping), then P-type impurity ions are implanted into source and drain regions and the LDD regions, and finally thermal annealing or optical annealing (or both) is performed to improve the crystallinity of the silicon film and activate impurities.

[0079] Manufacturing steps of this embodiment are almost the same as those in the fourth embodiment. This embodiment is different from the fourth embodiment in that the LDD regions 302 are doped with boron, as well as phosphorus, at a concentration of 3×10¹⁷ to 3×10¹⁸ atoms/cm³ that is higher than that of phosphorus. The doping of boron inverts the conductivity type of the LDD regions 302 from an N-type to a P-type. The source and drain regions 301 are doped with boron, instead of phosphorus, at 3×10¹⁹ to 1×10²¹ atoms/cm³, and therefore assume P-type conductivity.

[0080] The concentration of phosphorus in the LDD regions 302 is lower than that of boron in the source and drain regions 301 by 2 to 4 orders, the conductivity type of the LDD regions 302 can be inverted from an N-type to a P-type by introducing boron at a lower dose than that of the source and drain regions 301 is inverted. In inverting the conductivity type of the LDD regions 302 from an N-type to a P-type, the dose is so adjusted that the maximum concentration of boron implanted in the LDD regions 302 minus that of phosphorus implanted in those regions becomes 3×10¹⁷ to 3×10¹⁸ atoms/cm³.

[0081] In this embodiment, in producing the P-type TFT, not only the impurity that imparts P-type conductivity such as boron but also nickel and phosphorus are introduced into the active layer made of a crystalline silicon film. Therefore, a silicon film having good crystallinity can be obtained at a low temperature in a short time due to the catalyst effect of nickel.

[0082] Nickel in the channel 300 is transferred into LDD regions 302 and source and drain regions 301 by the gettering function of phosphorus. Thereby, concentration of nickel in the channel region 300 can be reduced.

[0083] As a result, this embodiment can produce TFTs having superior electrical characteristics whose variations among devices are small.

[0084] Embodiment 6

[0085] This embodiment is directed to a method of producing a P-type semiconductor device having superior characteristics in manufacturing a thin-film transistor having a LDD structure by using a crystalline silicon film into which nickel as a catalyst element for accelerating crystallization has been introduced. More specifically, ions including phosphorus ions are implanted into source and drain regions and LDD regions by known ion doping (also called plasma doping), then P-type impurity ions are implanted into the source and drain regions and the LDD regions, and finally thermal annealing or optical annealing (or both) is performed to improve the crystallinity of the silicon film and activate impurities.

[0086] Manufacturing steps of this embodiment are almost the same as those in the fifth embodiment. This embodiment is different from the fifth embodiment in that the LDD regions 302 are doped with boron at a concentration of 3×10¹⁹ to 1×10²¹ atoms/cm³ that is higher than that of phosphorus. The LDD regions 302 are also doped with boron at a concentration of 3×10¹⁷ to 4×10¹⁸ atoms/cm³ that is higher than that of phosphorus. The doping of boron inverts the conductivity type of the source and drain regions 301 and the LDD regions 302 from an N-type to a P-type.

[0087] To this end, the doping conditions of boron are so determined that the maximum concentration of boron implanted in the source and drain regions 301 minus that of phosphorus implanted in those regions becomes 3×10¹⁹ to 1×10²¹ atoms/cm³, and that the maximum concentration of boron implanted in the LDD regions 302 minus that of phosphorus implanted in those regions becomes 3×10¹⁷ to 3×10¹⁸ atoms/cm³.

[0088] In this embodiment, in producing the P-type TFT, not only the impurity that imparts P-type conductivity such as boron but also nickel and phosphorus are introduced into the active layer made of a crystalline silicon film. Therefore, a silicon film having good crystallinity can be obtained at a low temperature in a short time due to the catalyst effect of nickel, and nickel can be gettered by phosphorus. As a result, this embodiment can produce TFTs having superior electrical characteristics whose variations among devices are small.

[0089] Embodiment 7

[0090] This embodiment is directed to a case of forming CMOS thin-film transistors in which an N-type thin-film transistor and a P-type thin-film transistor are combined complementarily. FIGS. 4A to 4H show a manufacturing process according to this embodiment. First, a silicon oxide film 402 as an undercoat film is deposited on a glass substrate (Corning 7059 or 1737) 401 at a thickness of, for instance, 2,000 Å, and a 500-Å-thick intrinsic (I-type) amorphous silicon film 403 is deposited thereon by plasma CVD.

[0091] Then, a very thin oxide film (not shown) is formed by oxidizing the surface of the amorphous silicon film 403 by UV oxidation. This oxide film improves the surface characteristics of the amorphous silicon film 403. Thereafter, an acetate salt solution containing nickel at 1 to 30 ppm, for instance, 10 ppm, is applied by spin coating and then dried to form a nickel acetate layer 404. It is noted that the nickel acetate layer 404 forms a complete layer. (FIG. 4A)

[0092] Subsequently, thermal annealing is performed at 550° C. for 4 hours in a nitrogen atmosphere, to crystallize the amorphous silicon film 403. In this heat treatment, the nickel acetate layer 404 is decomposed, and as nickel passes through the oxide film (not shown) and diffuses from the surface of the amorphous silicon film 403 to the undercoat silicon oxide film 402, crystallization of the amorphous silicon film 403 proceeds. After completion of the crystallization step, laser light may be applied to the substrate to improve the crystallinity of the crystallized silicon film.

[0093] If a metal element such as nickel exists in a crystallized silicon film at a higher concentration than 1×10¹⁹ atoms/cm³, silicon partly assumes metallic properties to lose its semiconductor characteristics. On the other hand, if the concentration of the metal element is lower than 1×10¹⁵ atoms/cm³, the effect of accelerating crystallization is not attained. Therefore, the concentration of nickel in the crystallized silicon film needs to be in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³. The nickel concentration of the acetate salt solution, the coating conditions of the acetate salt solution, and other conditions should be predetermined so as to attain the above nickel concentration in the crystallized silicon film.

[0094] As shown in FIG. 4B, the crystallized silicon film is etched into island-like silicon regions 405 and 406. The island-like silicon regions 405 and 406 will constitute active layers of N-type and P-type TFTs, respectively.

[0095] Thereafter, a 1,500-Å-thick silicon oxide film 407 is deposited by plasma CVD, and a 4,000-Å-thick aluminum film, which is to constitute gate electrodes 408 and 409, is deposited thereon by sputtering. Scandium is added in advance to the aluminum film at 0.2 wt % to suppress occurrence of hillocks and whiskers.

[0096] Then, the aluminum film is anodized in an electrolyte to form a dense anodic oxide film (not shown) of about 100 Å in thickness. After a photoresist mask 410 is formed on the dense anodic oxide film, the aluminum film is pattered, to form gate electrodes 408 and 409. (FIG. 4B)

[0097] As shown in FIG. 4C, the gate electrodes 408 and 409 are again anodized with the photoresist mask 410 left as it is. As an electrolyte, an acid solution containing citric acid, oxalic acid, chromic acid, or sulphuric acid at 3 to 20%, for instance, a 3%-aqueous solution of oxalic acid, is used. Since the photoresist mask 410 and the dense anodic oxide film (not shown) exist on the surface of the gate electrodes 408 and 409, porous anodic oxide films 411 and 412 are formed on only the side faces of the gate electrodes 408 and 409. The length of the lightly doped impurity regions (LDD regions) is determined by the length of growth of the porous anodic oxide films 411 and 412, which can be controlled by the anodic oxidation processing time. In this embodiment, the porous anodic oxide films 411 and 412 are grown to have a length of 7,000 Å. (FIG. 4C)

[0098] After elimination of the photoresist mask 410, the gate electrodes 408 and 409 are again subjected to anodic oxidation, to form dense, strong anodic oxide films 413 and 414. In this embodiment, an electrolyte is prepared by neutralizing a ethylene glycol solution containing tartaric acid at 3% with an aqueous solution of ammonia to pH 6.9. (FIG. 4D)

[0099] Subsequently, a silicon oxide film 407 is etched with the porous anodic oxide films 411 and 412 and the dense anodic oxide films 413 and 414 as a mask, to form gate insulating films 415 and 416. Either wet etching or dry etching can be used as long as it can etch the silicon oxide film 407 without etching the anodic oxide films 411 to 414. In this embodiment, the silicon oxide film 407 is etched by dry etching that uses a ClF₃ gas.

[0100] As shown in FIG. 4E, the dense anodic oxide films (not shown) and the porous anodic oxide films 411 and 412 are sequentially removed. The dense anodic oxide films (not shown) are removed with buffer hydrofluoric acid, and the porous anodic oxide films 411 and 412 are removed with a mixed acid of phosphoric acid, acetic acid and nitric acid. Since the porous anodic oxide films 411 and 412 can be removed easily, the dense, strong anodic oxide films 413 and 414 are never etched.

[0101] Then, impurities are implanted into the island-like silicon regions 405 and 406 by ion doping with the gate electrodes 408 and 409 used as a mask. In this embodiment, phosphine (PH₃) that is diluted with hydrogen to 1 to 10% is used as a doping gas to implant phosphorus first. The substrate is kept at the room temperature during the doping. The doping conditions such as the acceleration voltage, the dose, and the number of times of doping are properly set so as to allow the gate insulating films 415 and 416 to serve as a semi-transmissive mask.

[0102] The exposed portions of the island-like silicon regions 405 and 406 are doped with phosphorus ions at a high concentration, to form N-type heavily doped impurity regions 417 to 420, which become source and drain regions of TFTs. Since the portions right under the gate electrodes 408 and 409 are not doped with phosphorus ions, they become channel forming regions 421 and 422. As for the portions that are covered with only the gate insulating films 415 and 416, phosphorus ions are interrupted by the gate insulating films 415 and 416 and implanted into these portions by only a small amount. Therefore, these portions constitute N-type lightly doped impurity regions 423 to 426. (FIG. 4E)

[0103] In the above doping step, the doping conditions are so set that the concentration of phosphorus ions in the N-type heavily doping impurity regions 417 to 420 becomes 3×10¹⁹ to 1×10²¹ atoms/cm³, and that the concentration of phosphorus ions in the lightly doped impurity regions 423 to 426 becomes 4×10¹⁶ to 7×10¹⁷ atoms/cm³.

[0104] Subsequently, as shown in FIG. 4F, a resist film is formed, and its portion covering the region to become a P-type TFT is removed by patterning to leave a resist mask 427. Boron as an impurity to impart P-type conductivity is then implanted by ion doping. Diborane (B₂H₆) that is diluted with hydrogen to 5% is used as a doping gas. The substrate is kept at the room temperature during the ion doping. As a result, in the island-like silicon region 406, the N-type conductivity of the heavily doped impurity regions 419 and 420 and the lightly doped impurity regions 425 and 426 is inverted to P-type conductivity; that is, P-type heavily doped impurity regions 428 (source) and 429 (drain) and P-type lightly doped impurity regions 430 and 431 are formed. On the other hand, the N-type conductivity of the heavily doped impurity regions 417 (source) and 418 (drain) and the lightly doped impurity regions 423 and 424 is maintained.

[0105] The doping conditions are so determined that the concentration of boron in the P-type heavily doped impurity regions 428 and 429 (source and drain regions) becomes higher than that of phosphorus in those regions by 3×10¹⁹ to 1×10²¹ atoms/cm³, and that the concentration of boron in the P-type lightly doped impurity regions 430 and 431 becomes higher than that of phosphorus in those regions by 3×10¹⁷ to 4×10¹⁸ atoms/cm³.

[0106] As shown in FIG. 4G, after the resist mask 214 is removed, laser annealing is performed to activate the introduced impurities and to restore the crystallinity of the island-like silicon regions 405 and 406 that have been damaged in the doping steps.

[0107] In this embodiment, the N-type or P-type source and drain regions 417, 418, 428 and 429 are doped with phosphorus at a concentration of 1×10²⁰ to 1×10²¹ atoms/cm³, and the N-type or P-type lightly doped regions 423, 424, 430 and 431 are doped with phosphorus at a concentration of 4×10¹⁶ to 7×10¹⁷ atoms/cm³. Therefore, nickel can be effectively gettered by phosphorus upon laser light illumination.

[0108] Where KrF excimer laser light (wavelength: 248 nm) is used, to getter nickel effectively, it is preferred that the laser light illumination conditions be such that the energy density is 200 to 400 MJ/cm², for instance, 250 mJ/cm², each point receives 2 to 20 shots of laser light, and the substrate temperature during the laser light illumination is set at 200° C.

[0109] After the laser annealing, thermal annealing is performed at 350° C. for 2 hours in a nitrogen atmosphere. Although both laser annealing and thermal annealing are performed in this embodiment, only one of those may be performed.

[0110] As shown in FIG. 4H, a 1-μm-thick silicon oxide film as an interlayer insulating film 432 is deposited by plasma CVD, and contact holes are formed therein. Source and drain electrodes/wiring lines 433 to 435 are formed through the contract holes by using a metal material such as a multi-layer film of a titanium film and an aluminum film. Finally, a heat treatment is performed at 350° C. for 2 hours in a hydrogen atmosphere. With the above steps, CMOS thin-film transistors are completed. (FIG. 4H)

[0111] Although in this embodiment boron ions are introduced after the phosphorus ion implantation, they may be introduced before the phosphorus ion implantation. In the latter case, as shown in FIG. 4F, boron ions are introduced in a state that the N-type TFT region is covered with a resist mask 427. Phosphorus ions may be introduced after the resist mask 427 is removed.

[0112] The invention enables formation of thin-film transistors in which off-currents are small and variations in characteristics are small, even with the use of a crystalline silicon film into which a catalyst element for accelerating crystallization has been introduced.

[0113] In particular, where nickel is used as the catalyst element for accelerating crystallization, the above effects of the invention is remarkable. The above effects are particularly advantageous in forming a plurality of devices having the same functions on the same substrate. This is because an off-current variation among devices causes unevenness in characteristics among the devices. Such unevenness is particularly harmful to pixels that are formed in a TFT liquid crystal display device. Thus, the invention is believed very useful in the industrial point of view. 

What is claimed is:
 1. A method for manufacturing a N-channel type semiconductor device comprising: forming a silicon film over an insulating substrate; crystallizing said silicon film with a catalyst material for accelerating crystallization, said crystallized silicon film comprising a channel region; introducing phosphorus ions into said crystallized silicon film to form source and drain regions therein, said phosphorus serving as a N-type impurity and a gettering material for said catalyst in said channel region; and annealing said crystallized silicon film to activate said introduced phosphorus and cause said phosphorus to serve as said gettering material; wherein said gettering materials in said source and drain regions remove said catalyst in said channel region.
 2. The method of claim 1 wherein said catalyst in said channel region is transferred from said channel region to said source and drain regions by said gettering materials, so that concentration of said catalyst in said channel region be lower than that of said source and drain regions.
 3. The method of claim 1 wherein said crystallization is performed by a thermal annealing or a laser annealing.
 4. The method of claim 1 wherein said annealing is one of a thermal annealing and a laser annealing.
 5. The method of claim 1 further comprising the steps of; forming a gate insulating film on said crystallized silicon film; and forming a gate electrode on said gate insulating film; wherein said phosphorus ions are introduced into said crystallized silicon film by using said gate electrode as a mask.
 6. The method of claim 1 wherein said catalyst material comprises a nickel, concentration thereof being in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³.
 7. A method for manufacturing a P-channel type semiconductor device comprising: forming a silicon film over an insulating substrate; crystallizing said silicon film with a catalyst material for accelerating crystallization, said crystallized silicon film comprising a channel region; introducing P-type impurity ions into said crystallized silicon to form source and drain regions therein; introducing phosphorus ions into said source and drain regions, said phosphorus serving as a gettering material for said catalyst in said channel region; and annealing said crystallized silicon film to activate said introduced P-type impurity and cause said phosphorus to serve as said gettering material; wherein said gettering materials in said source and drain regions remove said catalyst in said channel region.
 8. The method of claim 7 wherein said catalyst in said channel region is transferred from said channel region to said source and drain regions by said gettering materials, so that concentration of said catalyst in said channel region be lower than that of said source and drain regions.
 9. The method of claim 7 wherein said crystallization is performed by a thermal annealing or a laser annealing.
 10. The method of claim 7 wherein said annealing is one of a thermal annealing and a laser annealing.
 11. The method of claim 7 further comprising the step of; forming a gate insulating film on said crystallized silicon film; and forming a gate electrode on said gate insulating film; wherein said phosphorus ions and said P-type impurity ions are introduced into said source and drain regions by using said gate electrode as a mask.
 12. The method of claim 7 wherein said catalyst material comprises a nickel, concentration thereof being in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³.
 13. The method of claim 7 wherein concentration of said P-type impurity in said source and drain regions is higher than that of said phosphorus.
 14. A method for manufacturing a complementary semiconductor device consisting of N-channel and P-channel type transistors comprising: forming a silicon film over an insulating substrate; crystallizing said silicon film with a catalyst material for accelerating crystallization; forming a pair of active regions from said crystallized silicon film, said active region including a channel region and source and drain regions; introducing phosphorus ions into said active regions, said phosphorus serving as a N-type impurity and a gettering material for said catalyst in said channel region; selectively introducing P-type impurity ions into one of said active regions; and annealing said active regions to activate said introduced phosphorus and said P-type impurity and cause said phosphorus to serve as said gettering material; wherein said gettering materials in said source and drain regions remove said catalyst in said channel regions.
 15. The method of claim 14 wherein said catalysts in said channel region are transferred from said channel region to said source and drain regions by said gettering materials, so that concentration of said catalyst in said channel region be lower than that of said source and drain regions.
 16. The method of claim 14 wherein said crystallization is performed by a thermal annealing or a laser annealing.
 17. The method of claim 14 wherein said annealing is one of a thermal annealing and a laser annealing.
 18. The method of claim 14 further comprising the step of; forming gate insulating films on said active regions; and forming gate electrodes on said gate insulating films; wherein said phosphorus ions and said P-type impurity ions are introduced into said active regions by using said gate electrodes as masks.
 19. The method of claim 14 wherein said catalyst material comprises a nickel, concentration thereof being in a range of 1×10¹⁵ to 1×10¹⁹ atoms/cm³.
 20. The method of claim 14 wherein concentration of said introduced P-type impurity is higher than that of said phosphorus.
 21. A method for manufacturing a N-channel type semiconductor device comprising: forming a silicon film over an insulating substrate; crystallizing said silicon film with a catalyst material for accelerating crystallization; forming an active region including a channel region from said crystallized silicon film; introducing phosphorus ions into said active region to form first and second impurity regions, said first impurity regions serving as source and drain regions and said second impurity region being positioned between said source and drain regions and said channel region and; annealing said active region to activate said introduced phosphorus and cause said phosphorus to getter said catalyst material so that said gettering materials in said source and drain regions remove said catalyst in said channel regions; wherein concentration of said second impurity region is lower than that of said first impurity region.
 22. A method for manufacturing a P-channel type semiconductor device comprising: forming a silicon film over an insulating substrate; crystallizing said silicon film with a catalyst material for accelerating crystallization; forming an active region including a channel region from said crystallized silicon film; introducing P-type impurity ions into said active region to form first and second impurity regions, said first impurity regions serving as source and drain regions and said second impurity region being positioned between said source and drain regions and said channel region; introducing phosphorus ions into said first and second impurity regions, respectively; and annealing said active region to activate said introduced P-type impurity and cause said phosphorus to getter said catalyst material so that said gettering materials in said source and drain regions remove said catalyst in said channel regions; wherein concentrations of said P-type impurity and said phosphorus in said second impurity region are lower than these of said first region.
 23. A method for manufacturing a complementary semiconductor device consisting of N-channel and P-channel transistors comprising: forming a silicon film over an insulating substrate; crystallizing said, silicon film with a catalyst material for accelerating crystallization; forming a pair of active regions from said crystallized silicon film, said active region comprising a channel region; introducing phosphorus ions into said active regions to form first and second impurity regions respectively, said first impurity regions serving as source and drain regions and said second region being positioned between said first region and said channel region; selectively introducing P-type impurity ions into one of said active regions, said P-type impurity being introduced into said first and second impurity regions thereof; and annealing said active regions to activate said introduced phosphorus and said P-type impurity and cause said phosphorus to getter said catalyst material so that said gettering materials in said source and drain regions remove said catalyst in said channel regions; wherein concentrations of said P-type impurity and said phosphorus in said second impurity region are lower than these of said first impurity region.
 24. A semiconductor device for a P-channel type transistor comprising: a silicon film formed over an insulating substrate; and source and drain regions formed in said silicon film; and a channel region positioned between said source and drain regions; wherein a catalyst material, phosphorus and P-type impurity are incorporated in said source and drain regions, respectively.
 25. The device of claim 24 wherein said catalyst material serves as a crystallization accelerating material for said silicon film and phosphorus serves as a gettering material for removing said catalyst in said channel region.
 26. A semiconductor device for a complementary MOS transistors comprising: first and second active regions formed on an insulating substrate, said active region comprising a channel region; first impurity regions formed in said first active region, a catalyst material and phosphorus being incorporated therein; and second impurity regions formed in said second active region, a catalyst material, phosphorus and P-type impurity being incorporated therein.
 27. The device of claim 26 wherein said catalyst material serves as a crystallization accelerating material for said silicon and phosphorus serves as a gettering material for removing said catalyst in said channel region.
 28. A semiconductor device for a P-channel type transistor comprising: a silicon film formed over an insulating substrate, said silicon film including a channel region; first impurity regions formed in said silicon film; second impurity regions formed in said silicon film, said second region being positioned between said first region and said channel region; wherein a catalyst material, phosphorus and P-type impurity are incorporated in said first and second impurity regions, respectively.
 29. The device of claim 28 wherein said catalyst material serves as a crystallization accelerating material for said silicon film and phosphorus serves as a gettering material for removing said catalyst in said channel region, and concentrations of said P-type impurity and said phosphorus in said second impurity region are lower than these of said first region.
 30. A semiconductor device for a complementary MOS transistors comprising: first and second active regions formed on an insulating substrate, said active region comprising a channel region; first and second impurity regions formed in said first active region, a catalyst material and phosphorus being incorporated therein; and third and fourth impurity regions formed in said second active region, a catalyst material, phosphorus and P-type impurity being incorporated therein.
 31. The device of claim 30 wherein said catalyst material serves as a crystallization accelerating material for said silicon, and phosphorus serves as a gettering material for removing said catalyst in said channel region.
 32. The device of claim 30 wherein concentrations of said phosphorus in said second impurity region are lower than that of said first region, and concentrations of said P-type impurity and said phosphorus in said forth impurity region are lower than these of said third region. 